http://cicese.repositorioinstitucional.mx/jspui/handle/1007/4151| Estudio sobre las propiedades de emisión de nanodiamantes con centros nitrógeno-vacancia Study on the emission properties of nanodiamonds with nitrogen-vacancy centers | |
| Napoleón Enrique Granados Umanzor | |
| KARINA GARAY PALMETT | |
| Acceso Abierto | |
| Atribución | |
| Fuente de fotones individuales, Nanodiamantes, Centros NV, Fluorescencia Single photon source, Nanodiamonds, NV centers, Fluorescence | |
| En este trabajo se estudian las propiedades de emisión de nanodiamantes con centros nitrógeno-vacancia, con el objetivo principal de demostrar que éstos pueden actuar como una fuente de fotones individuales. Se caracterizó la fluorescencia de los nanodiamantes al ser irradiados por luz láser bajo dos regímenes de excitación: pulsada (centrada en 513.7 nm) y continua (centrada en 532 nm). Como resultado, se obtuvieron mapas de fluorescencia óptimos, en los cuales se puede distinguir la presencia de posibles nanodiamantes con centros nitrógeno-vacancia. Además, se midió el espectro de fluorescencia en los rangos de 550 nm a 700 nm y de 550 nm a 800 nm para los regímenes pulsado y continuo, respectivamente. Finalmente, se implementó un arreglo interferométrico del tipo Hanbury Brown & Twiss que permite medir la función de correlación de segundo orden a retraso cero, tras lo cual se pudo validar el carácter no clásico de una fuente identificada. In this work, the emission properties of nanodiamonds with nitrogen-vacancy centers are studied, with the main objective of demonstrating that they can act as a source of single photons. The nanodiamonds fluorescence was characterized by laser light irradiation under two excitation regimes: pulsed (centered at 513.7 nm) and continuous (centered at 532 nm). As a result, optimal fluorescence maps were obtained, and possible nanodiamonds with nitrogen-vacancy centers were distinguished. Furthermore, the fluorescence spectrum was measured in the ranges of 550 nm to 700 nm and 550 nm to 800 nm for the pulsed and continuous regimen, respectively. Finally, an interferometric arrangement of the Hanbury Brown and Twiss type was implemented that allows measuring the second-order correlation function at zero delay, after which the non-classical character of an identified source was validated. | |
| CICESE | |
| 2024 | |
| Tesis de maestría | |
| Español | |
| Granados Umanzor, N.E. 2024. Estudio sobre las propiedades de emisión de nanodiamantes con centros nitrógeno-vacancia. Tesis de Maestría en Ciencias. Centro de Investigación Científica y de Educación Superior de Ensenada, Baja California. 57 pp. | |
| OPTICA FÍSICA | |
| Aparece en las colecciones: | Tesis - Óptica |
Cargar archivos:
| Fichero | Descripción | Tamaño | Formato | |
|---|---|---|---|---|
| tesis_Napoleón Enrique Granados Umanzor_20 ago 2024_BIBcorregido.pdf | Descripción completa de la tesis | 2.27 MB | Adobe PDF | Visualizar/Abrir |